| 单位：mm | ||||||||||
| 公称直径d | M4 | M5 | M6 | M8 | M10 | M12 | M16 | M20 | M24 | |
| 螺距P | 0.7 | 0.8 | 1 | 1.25 | 1.5 | 1.75 | 2 | 2.5 | 3 | |
| d1 | max | 8 | 11 | 13 | 16 | 20 | 23 | 29 | 35 | 44 |
| min | 6 | 8 | 10 | 13 | 17 | 20 | 26 | 32 | 41 | |
| d2 | max | 7 | 9 | 11 | 12.5 | 16.5 | 19.5 | 23 | 29 | 37.5 |
| min | 5.5 | 7.5 | 9 | 10.5 | 14.5 | 17.5 | 21 | 27 | 35 | |
| L | max | 20 | 26 | 33 | 39 | 51 | 65 | 73 | 90 | 110 |
| min | 18 | 24 | 30 | 36 | 48 | 62 | 70 | 86 | 106 | |
| k | max | 10.5 | 13 | 17 | 20 | 25 | 33.5 | 37.5 | 46.5 | 56.5 |
| min | 8.5 | 11 | 15 | 18 | 23 | 31 | 35 | 44 | 53.5 | |
| y | max | 1.9 | 2.3 | 2.3 | 2.8 | 4.4 | 4.9 | 6.4 | 6.9 | 9.4 |
| min | 1.1 | 1.5 | 1.5 | 2 | 3.6 | 4.1 | 5.6 | 6.1 | 8.6 | |
| m | max | 4.6 | 6.5 | 8 | 10 | 12 | 14 | 17 | 21 | 25 |
| min | 3.2 | 4 | 5 | 6.5 | 8 | 10 | 13 | 16 | 20 | |
| 化学成分，%,max | ||||||||||
| 组别 | C | Si | Mn | P | S | Cr | Mo | Ni | Cu | 特性 |
| 304-A2 | 0.1 | 1 | 2 | 0.05 | 0.03 | 15-20 | 8-19 | 4 |
加工硬化率适中，适于一般的冷间加工以及伸抽，冷加工性能较好，普遍用于外六角螺钉、螺母以及垫圈产品 |
|
| 316-A4 | 0.08 | 1 | 2 | 0.045 | 0.03 | 16-18.5 | 2-3 | 10-15 | 1 |
加钼，耐腐蚀能力较304强，特别适用于海水及化学介质，更加的耐腐蚀性及耐孔蚀性。 |
|
注： 1)如镍含量低于8%,则锰的最小含量必须为5% |
||||||||||
| 机械性能 | |||||||||||
| 类别 | 组别 | 性能等级 | 螺丝直径 | 抗拉强度mpa/mm2 | 规定非比列伸长应为mpa/mm2 | 断后伸长量mpa/mm2 | |||||
| 奥氏体 | A2，A4 | 50 |
≤ 39 |
500 | 210 | 0.6d | |||||
| 70 |
≤ 24 |
700 | 450 | 0.4d | |||||||
| 80 |
≤ 24 |
800 | 600 | 0.3d | |||||||