| 单位：mm | |||||
| 公称直径D | 螺距P | m | S | ||
| max | min | max | min | ||
| M1 | 0.25 | 0.8 | 0.55 | 2.5 | 2.4 |
| M1.2 | 0.25 | 1 | 0.75 | 3 | 2.9 |
| M1.4 | 0.3 | 1.2 | 0.95 | 3 | 2.9 |
| M1.6 | 0.35 | 1.3 | 1.05 | 3.2 | 3.02 |
| M1.7 | 0.35 | 1.4 | 1.15 | 3.5 | 3.38 |
| M2 | 0.4 | 1.6 | 1.35 | 4 | 3.82 |
| M2.3 | 0.45 | 1.8 | 1.55 | 4.5 | 4.32 |
| M2.5 | 0.45 | 2 | 1.75 | 5 | 4.82 |
| M2.6 | 0.45 | 2 | 2.15 | 5 | 4.82 |
| M3 | 0.5 | 2.4 | 2.55 | 5.5 | 5.32 |
| M3.5 | 0.6 | 2.8 | 2.9 | 6 | 5.82 |
| M4 | 0.7 | 3.2 | 3.7 | 7 | 6.78 |
| M5 | 0.8 | 4 | 3.7 | 8 | 7.78 |
| M6 | 1 | 5 | 4.7 | 10 | 9.78 |
| M7 | 1 | 5.5 | 5.2 | 11 | 10.73 |
| M8 | 1/1.25 | 6.5 | 6.14 | 13 | 12.73 |
| M10 | 1/1.25/1.5 | 8 | 7.64 | 17 | 16.73 |
| M12 | 1.25/1.5/1.75 | 10 | 9.64 | 19 | 18.67 |
| M14 | 1.5/2 | 11 | 10.3 | 22 | 21.67 |
| M16 | 1.5/2 | 13 | 12.3 | 24 | 23.67 |
| M18 | 1.5/2/2.5 | 15 | 14.3 | 27 | 26.16 |
| M20 | 1.5/2/2.5 | 16 | 14.9 | 30 | 29.16 |
| M22 | 1.5/2/2.5 | 18 | 16.9 | 32 | 31 |
| M24 | 2/3 | 19 | 17.7 | 36 | 35 |
| M27 | 2/3 | 22 | 20.7 | 41 | 40 |
| M30 | 2/3.5 | 24 | 20.7 | 46 | 45 |
| 化学成分，%,max | ||||||||||
| 组别 | C | Si | Mn | P | S | Cr | Mo | Ni | Cu | 特性 |
| 304-A2 | 0.1 | 1 | 2 | 0.05 | 0.03 | 15-20 | 8-19 | 4 |
加工硬化率适中，适于一般的冷间加工以及伸抽，冷加工性能较好，普遍用于外六角螺钉、螺母以及垫圈产品 |
|
| 316-A4 | 0.08 | 1 | 2 | 0.045 | 0.03 | 16-18.5 | 2-3 | 10-15 | 1 |
加钼，耐腐蚀能力较304强，特别适用于海水及化学介质，更加的耐腐蚀性及耐孔蚀性。 |
|
注： 1)如镍含量低于8%,则锰的最小含量必须为5% |
||||||||||
| 机械性能 | |||||||||||
| 类别 | 组别 | 性能等级 | 螺丝直径 | 抗拉强度mpa/mm2 | 规定非比列伸长应为mpa/mm2 | 断后伸长量mpa/mm2 | |||||
| 奥氏体 | A2，A4 | 50 |
≤ 39 |
500 | 210 | 0.6d | |||||
| 70 |
≤ 24 |
700 | 450 | 0.4d | |||||||
| 80 |
≤ 24 |
800 | 600 | 0.3d | |||||||